    Reactive Emulsifiers

    ➣tip1: Mixture ratio of prepolymer and emulsifier can be at 5:1.
    ➣tip2: Phosphate emulsifiers can obtain stable emulsion,and also have good 
    dispersion.
    ➣tip3: Aggolomerate and oligomers maybe occur when adding quickly or under 
    high-temperature.
    ➣tip4: High dosage is beneficial to improve the water-resistance of the film.
    没有此类产品
    Products Detail
    reactive surfactant
    Ionic pattern
    Chemical name
    Solid fraction(WT%)
    Critical micelle concentration(%)
    Surface tension(mN/m)
    无APEO
    Characteristic
    Nonionic
    Allyl polyether
    99%min
    -
    -
    Reactive active group, copolymerized with acrylic monomers
    Excellent solubility and dispersibility
    It can emulsify monomers (except AE-100) and has good compatibility with high electrolyte.
    Improving the ability of emulsion to resist calcium chloride
    Hydrophilic Modification by Solvent Copolymerization
    Nonionic
    Polyether Containing Double Bond Groups
    99%min
    -
    -
     
    Nonionic
    Polyether Containing Double Bond GroupsEO=10
    99%min
    -
    -
    Nonionic
    Polyether Containing Double Bond GroupsEO=20
    98%min
    -
    -
    Nonionic
    Polyether Containing Double Bond GroupsEO=20
    17.5-18.5%
    0.15-0.2
    41.6
    Nonionic
    Polyether Containing Double Bond GroupsEO=30
    98%min
    -
    -
    anion
    Acrylic polyether phosphate
    98%min
    -
    -
    Copolymer monomers to enhance the flexibility and cohesion of coatings
    Characteristic of phosphoric acid group, excellent dispersibility of pigments and fillers, good adhesion of substrates
    It can improve the hydrolytic stability of emulsion system.
    Improving waterproofing and scrubbing resistance
    anion
    Methacrylic acid polyether phosphate
    98%min
    -
    -
    anion
    Alcohol ether phosphate containing double bonds
    96% min
    anion
    Methacrylamide isopropyl sulfonic acid
    98%min
    -
    -
    It can not emulsify monomer, improve waterproof and scrubbing properties, improve pigment acceptability, and improve adhesion. It can improve mechanical stability and hydrolytic stability of emulsion system.
    anion
    Sodium methacrylamide isopropyl sulfonate
    48-51%
    -
    -
    anion
    Ammonium methacrylamide isopropyl sulfonate
    48-51%
    -
    -
    anion
    Alkyl alcohol ether sulfate containing allyl group
    49-51%
    0.08-0.15
    36

    Emulsifying monomer
    Low active agent dosage in emulsification(1—3%max)
    Solid content of high emulsion (above 50%)
    Excellent mechanical stability
    Give the emulsion good water resistance, in which NRS-1225 has longer alkyl chain than NRS-1025 and M-12S than M-10S, and finer particle size.
    anion
    Alkyl alcohol ether sulfate containing allyl group
    24-26%
    0.08-0.15
    36
    anion
    Alkyl alcohol ether sulfate containing double bond group
    24-26%
    0.025-0.075
    40.9
    anion
    Dialkyl sulfosuccinate salts containing double bonds
    39-42%
    0.1-0.2
    31
    anion
    Dialkyl sulfosuccinate salts containing double bonds
    24-26%
    0.05-0.1
    27.3
    anion
    Dialkyl sulfosuccinate salts containing allyl group
    49-52%
    0.05-0.08
    27.1
    anion
    Alkyl Sulfosuccinate Salts Containing Allyl Group
    39-42%
    0.075-0.1
    29.8
    anion
    Alkyl Alcohol Ether Sulfosuccinate Diester Sodium Salt Containing Allyl Group
    39-42%
    0.05-0.1
    33.5
    anion
    Dialkyl sulfosuccinate salts containing double bonds
    37-39%
    0.025-0.075
    26.9
    anion
    Dialkyl sulfosuccinate salts containing double bonds
    49-51%
    0.025-0.05
    25
    anion
    Vinyl sulfonate
    33-37%
    -
    -
    Improving the stability of emulsion by comonomer
    anion
    Sodium 1-propoxy 2-hydroxypropane sulfonate
    41-44%
    -
    -
    Improve the waterproof and scrubbing properties of the paint film, improve the stability of the emulsion and reduce the gel amount during the polymerization process.
    anion
    Alcohol ether phosphate containing double bonds
    39-41%
    It can copolymerize with vinyl acetate, styrene and acrylic monomers to improve the waterproof and scrubbing resistance of the paint film, the acceptance of the pigment and the adhesion.
    It can improve the mechanical stability, hydrolytic stability of the emulsion system, and reduce the gel amount of polymerization process.
    anion
    Specially made Alcohol ether phosphate containing double bonds
    39-41% 
    anion
    Ammonium polyether sulfate containing double bond group
    49-52%
    -
    -
      Give the emulsion excellent stability, so that the emulsion coating has good water resistance and copolymerization properties.
    anion
    Polyether sulfate containing allyl alkoxy group
    49-52%
    0.025-0.06
    40
     
    The emulsion has excellent emulsifying ability and gives excellent stability to the emulsion. The emulsion film has good water resistance and excellent copolymerization properties, resulting in extremely low APEO content. V-1025S has good polymerization performance with styrene-containing monomers.
    anion
    Alkyl propylene phenoxy polyether sulfate
    24-26%
    0.05-0.15
    38.9
     
    anion
    Allyl polyether phosphate
    99%
    0.1-0.2
    33
    It has good solubility and dispersibility, & nbsp; can be grafted onto the polymer chain in the reaction, thus forming a unique dispersion protection structure.
    anion
    Ammonium polyether phosphate containing double bonds
    98%
    0.02-0.08
    35
     

     

    Corresponding parameter set not found, please add it in property template of background